Analysis of in-vitro reaction layers formed on plasma sprayed bioglass-titanium coatings

Goller G., Yazici T., Oktar F., Demirkesen E., Kayali E.

EURO CERAMICS VIII, PTS 1-3, ss.1973-1976, 2004 (SCI-Expanded) identifier

  • Yayın Türü: Makale / Tam Makale
  • Basım Tarihi: 2004
  • Dergi Adı: EURO CERAMICS VIII, PTS 1-3
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED)
  • Sayfa Sayıları: ss.1973-1976
  • Marmara Üniversitesi Adresli: Hayır

Özet

Bioglass, 45S5 containing 45% SiO2, 6% P2O5, 24.5%, CaO and 24.5% Na2O all in weight percent, was plasma sprayed onto a titanium substrate with and without 60Al(2)O(3) 40TiO(2) as a bond coating. It has been observed that there is a uniform coating layer with a thickness of 110 mum and that there was not any reaction observed at the coating-metal interface for both coating application. In vitro assessment of bio-activity was carried out by immersing in Simulated Body Fluid (SBF). Fourier transform infrared spectroscopy and thin film X-ray diffraction techniques were used to analyze the inorganic carbonate apatite layer developed on coating in an in-vitro environment. Scanning electron microscopy was used to surface characterization.