Toughening of Epoxy Resin via Silane Terminated Urethane Including Pre-Hydrolyzed Tetraethoxysilane

Kartal İ.

ASIAN JOURNAL OF CHEMISTRY, cilt.26, sa.18, ss.6018-6022, 2014 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 26 Sayı: 18
  • Basım Tarihi: 2014
  • Doi Numarası: 10.14233/ajchem.2014.16485
  • Dergi Adı: ASIAN JOURNAL OF CHEMISTRY
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.6018-6022
  • Marmara Üniversitesi Adresli: Evet

Özet

In this Study, firstly; Silane terminated urethane was synthesized from poly(hexamethylene carbonate) diol and 3-isocyanatopropyl trimethoXysilane. Prepared solutions of inorganic part (silane terminated urethane + pre-hYdrolyzed tetraethoxysildne) were Mixed with epoxy-hardenet mixture to obtain hybrid solutions. Various hybrid Solutions were prepareclnsing different epoxy/inorganic part solution:compositions. Furthermore, ther'effect of silane terminated urethane on the mechanical and morphological properties of epoxy was investigated. The structure and pioperties of the composites are characterized using a scanning:electron Microscopy. Epoxy/silane, terminated I urethane hybrid materials were Subjected to examinations to obtain their tensile strength, three point bending properties, hardness, izod impact strength. Incorporation of silane terminated urethane into the epoxy resin greatly Modified the impact behavior of hybrids.