Effects of NCO/OH Ratio and Reactive Diluent Type on the Adhesion Strength of Polyurethane Methacrylates for Cord/Rubber Composites


Yildiz Z., Önen H. A., Gungor A., Wang Y., Jacob K.

POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING, cilt.57, sa.10, ss.935-944, 2018 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 57 Sayı: 10
  • Basım Tarihi: 2018
  • Doi Numarası: 10.1080/03602559.2017.1364382
  • Dergi Adı: POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.935-944
  • Anahtar Kelimeler: Adhesion strength, NCO:OH ratio, polyester cord, reactive diluent, styrene butadiene rubber, UV curing, POLYETHYLENE TEREPHTHALATE, WOOD ADHESIVE, ARAMID FIBERS, RUBBER, POLYMERIZATION, ACRYLATE, DENSITY, POLYOLS, SYSTEM
  • Marmara Üniversitesi Adresli: Evet

Özet

A series of dual curable polyurethane methacrylate-based oligomers were synthesized by changing the NCO:OH ratio and then were included in adhesive formulations using trimethylolpropane trimethacrylate and tricyclodecane dimethanol diacrylate (TCDDA) as reactive diluents. The effects of NCO:OH ratio and reactive diluent type on the structural properties of UV-cured free films and adhesion properties between polyester cord/rubber surfaces were studied. The highest adhesion strength of the 103Ncm(-1) was obtained when the NCO:OH ratio was set as 4 and the TCDDA was used as a reactive diluent.