Electrospun 3D Structured Carbon Current Collector for Li/S Batteries.

Kalybekkyzy S., Mentbayeva A., Yerkinbekova Y., Baikalov N., Kahraman M. V., Bakenov Z.

Nanomaterials (Basel, Switzerland), cilt.10, 2020 (SCI-Expanded) identifier identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 10
  • Basım Tarihi: 2020
  • Doi Numarası: 10.3390/nano10040745
  • Dergi Adı: Nanomaterials (Basel, Switzerland)
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, Aerospace Database, Agricultural & Environmental Science Database, Communication Abstracts, INSPEC, Metadex, Directory of Open Access Journals, Civil Engineering Abstracts
  • Anahtar Kelimeler: carbon nanofibers, lithium-sulfur battery, electrospinning method, electrode capacity, current collector, NEGATIVE ELECTRODE, COMPOSITE CATHODE, POLYACRYLONITRILE, SULFUR, PERFORMANCE, NANOFIBERS, LIGHTWEIGHT, BINDER, FIBERS, ANODE
  • Marmara Üniversitesi Adresli: Evet

Özet

Light weight carbon nanofibers (CNF) fabricated by a simple electrospinning method and used as a 3D structured current collector for a sulfur cathode. Along with a light weight, this 3D current collector allowed us to accommodate a higher amount of sulfur composite, which led to a remarkable increase of the electrode capacity from 200 to 500 mAh per 1 g of the electrode including the mass of the current collector. Varying the electrospinning solution concentration enabled obtaining carbonized nanofibers of uniform structure and controllable diameter from several hundred nanometers to several micrometers. The electrochemical performance of the cathode deposited on carbonized PAN nanofibers at 800 degrees C was investigated. An initial specific capacity of 1620 mAh g(-1) was achieved with a carbonized PAN nanofiber (cPAN) current collector. It exhibited stable cycling over 100 cycles maintaining a reversible capacity of 1104 mAh g(-1) at the 100th cycle, while the same composite on the Al foil delivered only 872 mAh g(-1). At the same time, 3D structured CNFs with a highly developed surface have a very low areal density of 0.85 mg cm(-2) (thickness of -25 mu m), which is lower for almost ten times than the commercial Al current collector with the same thickness (7.33 mg cm(-2)).