Electronic, transport, and magnetic properties of (Ca, Ba)(0.9)La0.1Fe1.9Pt0.1As2 compounds


Guler A. , Boyraz C. , Avci S., Arda L., Ozdemir M., Oner Y.

INTERNATIONAL JOURNAL OF MODERN PHYSICS B, cilt.33, sa.4, 2019 (SCI İndekslerine Giren Dergi) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 33 Konu: 4
  • Basım Tarihi: 2019
  • Doi Numarası: 10.1142/s0217979219500085
  • Dergi Adı: INTERNATIONAL JOURNAL OF MODERN PHYSICS B

Özet

Superconductivity and magnetic properties were studied for La and Pt substituted (Ca, Ba)(0.9)La0.1Fe1.9Pt0.1As2 samples using structural, resistivity and magnetic measurement techniques. All bulk samples were synthesized by solid-state reaction method and annealed under a specific annealing technique with a time-dependent annealing process in vacuumed quartz tubes. ThCr2Si2 -type crystal structure was concluded for both samples varying with in- and out-of-plane lattice parameters. The superconducting critical temperatures were determined by resistivity and under H=20 Oe magnetization measurements, which were performed between the temperature ranges of 0-200 K. The upper and lower critical fields were determined and possible Meissner effects were roughly figured out to understand the level of shielding from M-H measurements. The maximum critical temperature was obtained from Ca0.9La0.1Fe1.9Pt0.1As2.