Optimization of Physical and Mechanical Properties of the Meleagris Gallopova Hydroxyapatite Magnesium Oxide Composites by Gray Relational Analysis Method

Creative Commons License

Hartomacıoğlu S., Pazarlıoğlu S. S., Onat A., Salman S.

International Congrees on Engineering and Natural Sciences (ICENS 2015). Skopje, Makedonya, Skopje, Makedonya, 15 - 19 Mayıs 2015, cilt.1, sa.1, ss.313

  • Yayın Türü: Bildiri / Özet Bildiri
  • Cilt numarası: 1
  • Basıldığı Şehir: Skopje
  • Basıldığı Ülke: Makedonya
  • Sayfa Sayıları: ss.313
  • Marmara Üniversitesi Adresli: Evet

Özet

In the present study the effect of addition magnesium oxide to meleagris gallopova on physical and

mechanical properteis was optimazed by gray relational analysis method. The amount of magnesium

oxide was 5 and 10 wt%. Composites were wet milled, dried and compacted at 350 MPa. Compacted

samples were sintered at five different temperatures between 900oC and 1300oC. Density, hardness

and compressive strength measurements were carried out. Experimental results show that increment

magnesium oxide rate deal with increasing of all the properties of meleagris gallopova hydroxyapatite.

Optimum results were defined by gray relational analysis method